← Glossary

Solidification Crack

Hot cracking occurs due to mechanical stresses during cooling of steel that exceed the material's strength.

Physikalisch-chemischer Wirkmechanismus

During the cooling of steel, mechanical stresses arise due to the expansion and contraction of the body. These stresses can lead to cracks if they exceed the material's strength.

Metallurgical Relevance & Welding Risks

Hot cracks can occur with inadequate cooling or too high carbon content. They lead to fractures and reduce the service life of components.

Werkstattpraxis & Handlungsanweisungen

To avoid hot cracks, ensure controlled cooling and a low carbon content in the steel. Use stress relief processes if necessary.